DESCRIPTION
HAISO graphic films are high-performance coated films offering very good chemical and abrasion resistance together with unique processing characteristics. These highly durable easily printed films create new opportunities in graphic design with a unique package of benefits, flexible UV processing, multiple topside selective texturing, color topside texturing, durability of coating and texture adhesion when exposed to strong household chemicals such as wisk or formula 409#
HS 3096 film is available in 48” widths and gauges from .007’’ to .003”. masking is of the cling type on the uncoated side and of the stick type on the coated side
Typical property values
|
property |
Test method |
Units |
value |
|
physical |
|
|
|
|
Density |
ASTM D 792 |
|
1.2 |
|
Surface energy(1st/2ndsurface) |
ASTM D5946-01 |
|
36/34 |
|
Surface tension(1st/2ndsurface) |
Dyne pens |
dyne |
38-40/38-40 |
|
Pencil hardness(coated surface) |
ASTM D3363 |
|
Hb |
|
Taber abrasion |
ASTM D1044 |
Delta haze |
4 |
|
Area factor |
calculation |
M2/kg/mm |
0.833 |
|
HAZE |
ASTM D1003 |
% |
0.5 |
|
Light transmission |
ASTM D1003 |
% |
0.5 |
|
Yellowness index |
ASTM D192 |
|
1.0 |
|
Water absorption, equilibrium |
ASTM D570 |
% |
40 |
|
Resistance to humidity
720 hrs(1000F, 100% R .H) |
HAISO TEST |
-- |
-- |
|
GLOSS |
|
|
|
|
Backpainted, flat black
600
200 |
ASTM D523 |
Gardner |
90
84 |
|
Clear over white
600
200 |
ASTM D523 |
gardner |
167
184 |
|
Mechanical |
|
|
|
|
Tensile strength |
ASTM D882 (ISO 527) |
|
|
|
Yield |
|
Psi |
8500 |
|
Ultimate |
|
psi |
8800 |
|
Tear strength |
|
|
|
|
Initiation |
ASTM D 1004 |
Lb/mil |
1.4 |
|
Propogation |
ASTM D1922 |
g/mil |
30 |
|
thermal |
|
|
|
|
Vicat softening temperature B |
ASTM 1525 |
0C |
160 |
|
Heat deflection temp. byTMA at 1.8MPA |
ISO 75 modified |
0C |
145 |
|
Shrinkage at 150 0C |
ASTN D1204 |
% |
1.4% |
Manufacturing specifications
|
Norminal gauge ranges |
Min/mad limit of norminal |
|
0.25-0.375mm |
±10% |
|
0.5-0.75mm |
±5% | |